Stanyl? TW272B6

Manufacturer: Envalior/DSM
Produced At: Europe / China
Product Category: Polyamide 46（PA46）
Product No: Stanyl TW272B6
Product Quantity: 25KG / BAG
Product Features: Heat Stabilized，PTFE Lubricated

Product information

Stanyl? TW272B6

Polyamide 46

Product Description:

30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified

Special Features:

Heat stabilized or stable to heat

Wear and friction modified

Stanyl? is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.

Filler / Reinforcement	Carbon Fiber, 30% Filler by Weight
Additive	Heat StabilizerPTFE Lubricant
Features	Heat Stabilized
Processing Method	Injection Molding
Resin ID (ISO 1043)	(PA46+PTFE)-CF30

Physical	Dry	Conditioned	Unit	Test Method
Density	1.36	--	g/cm3	ISO 1183
Molding Shrinkage				ISO 294-4
Across Flow	0.60	--	%
Flow	0.30	--	%
Water Absorption				ISO 62
Saturation, 73°F	8.1	--	%
Equilibrium, 73°F, 50% RH	2.3	--	%
Viscosity Number	150	--	cm3/g	ISO 307

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus				ISO 527-2
--	3.48E+6	2.10E+6	psi
248°F	1.81E+6	--	psi
320°F	1.60E+6	--	psi
356°F	1.52E+6	--	psi
392°F	1.45E+6	--	psi
Tensile Stress				ISO 527-2
Break	34800	23200	psi
Break, 248°F	18900	--	psi
Break, 320°F	16000	--	psi
Break, 356°F	14500	--	psi
Break, 392°F	13100	--	psi
Tensile Strain				ISO 527-2
Break	1.6	3.5	%
Break, 248°F	3.1	--	%
Break, 320°F	3.1	--	%
Break, 356°F	3.1	--	%
Break, 392°F	3.1	--	%
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-22°F	2.9	2.9	ft·lb/in2
73°F	2.9	6.2	ft·lb/in2
Charpy Unnotched Impact Strength				ISO 179/1eU
-22°F	24	26	ft·lb/in2
73°F	24	38	ft·lb/in2

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)	554	--	°F	ISO 75-2/A
Glass Transition Temperature 3	167	--	°F	ISO 11357-2
Melting Temperature 3	563	--	°F	ISO 11357-3
CLTE				ISO 11359-2
Flow	1.4E-5	--	in/in/°F
Transverse	1.9E-5	--	in/in/°F

Injection	Dry	Unit
Drying Temperature	176	°F
Drying Time	4.0 to 8.0	hr
Rear Temperature	536 to 608	°F
Middle Temperature	572 to 608	°F
Front Temperature	572 to 608	°F
Nozzle Temperature	572 to 608	°F
Processing (Melt) Temp	581 to 608	°F
Mold Temperature	176 to 248	°F
Injection Rate	Moderate-Fast
Back Pressure	290 to 1450	psi
Screw Compression Ratio	2.5:1.0