Radilon? A USZ200 100 NAT
Polyamide 66
PA66 injection moulding grade. Toughened. Natural colour.
Suitable for parts requiring excellent impact resistance, even at low temperatures, and high flexibility.
Features | - Good Impact Resistance，High Flexibility，Low Temperature Impact Resistance
|
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.06 | -- | g/cm3 | ISO 1183 |
Molding Shrinkage 2 |
|
|
| ISO 294-4 |
Across Flow | 1.7 | -- | % |
|
Flow | 1.9 | -- | % |
|
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 7.0 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 1.8 | -- | % |
|
Tensile Modulus | 239000 | 123000 | psi | ISO 527-2/1A/1 |
Tensile Stress (Yield) | 5800 | 3630 | psi | ISO 527-2/1A/50 |
Tensile Strain (Yield) | 10 | 30 | % | ISO 527-2/1A/50 |
Nominal Tensile Strain at Break | 90 | > 100 | % | ISO 527-2/1A/50 |
Flexural Modulus 3 | 203000 | -- | psi | ISO 178 |
Flexural Stress 3 | 7980 | -- | psi | ISO 178 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 38 | -- | ft·lb/in2 |
|
73°F | 48 | 59 | ft·lb/in2 |
|
Heat Deflection Temperature (264 psi, Unannealed) | 149 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 356 | -- | °F | ISO 306/B50 |
Melting Temperature 4 | 500 | -- | °F | ISO 11357-3 |
Surface Resistivity 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index(Solution A) | 600 | -- | V | IEC 60112 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1200 | -- | °F | IEC 60695-2-12 |
Glow Wire Ignition Temperature(0.08 in) | 1250 | -- | °F | IEC 60695-2-13 |
Flammability | < 1 | -- | in/min | FMVSS 302 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 518 to 554 | °F |
|
Mold Temperature | 140 to 176 | °F |
|
Injection Rate | Moderate |
|
|