VICTREX? PEEK POLYMER AS110
High performance thermoplastic material, reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, colour natural/beige.
VICTREX? AS110 is typically used in applications that operate across a wide temperature range and require a combination of strength and ductility, good creep resistance and chemical resistance in aggressive fluid environments. Less abrasive on low-hardened light alloys compared to stiffer wear grades.
Material Properties |
Physical | Nominal Value | Unit | Test Method |
Density (Crystalline) | 1.41 | g/cm3 | ISO 1183 |
Spiral Flow 1 | 16.0 | cm | Internal Method |
Molding Shrinkage 2 |
|
| ISO 294-4 |
Across Flow | 1.1 | % |
|
Flow | 0.90 | % |
|
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 4700 | MPa | ISO 527-1 |
Tensile Stress (Break, 23°C) | 72.0 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 8.9 | % | ISO 527-2 |
Flexural Modulus (23°C) | 4100 | MPa | ISO 178 |
Flexural Stress (23°C) | 140 | MPa | ISO 178 |
Compressive Stress (23°C) | 130 | MPa | ISO 604 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact Strength (23°C) | 4.5 | kJ/m2 | ISO 180/A |
Unnotched Izod Impact Strength (23°C) | 20.0 | kJ/m2 | ISO 180 |
Hardness | Nominal Value | Unit | Test Method |
Shore Hardness (Shore D, 23°C) | 85.0 |
| ISO 868 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 155 | °C | ISO 75-2/Af |
Glass Transition Temperature |
|
| ISO 11357-2 |
Onset | 143 | °C |
|
Midpoint | 147 | °C |
|
Melting Temperature | 343 | °C | ISO 11357-3 |
CLTE - Flow |
|
| ISO 11359-2 |
< 143°C | 45 | ppm/K |
|
> 143°C | 120 | ppm/K |
|
CLTE - Average |
|
| ISO 11359-2 |
< 143°C | 50 | ppm/K |
|
> 143°C | 120 | ppm/K |
|
Thermal Conductivity |
|
| ISO 22007-4 |
23°C 3 | 0.30 | W/m/K |
|
23°C 4 | 0.32 | W/m/K |
|
Fill Analysis | Nominal Value | Unit | Test Method |
Melt Viscosity (400°C) | 225 | Pa·s | ISO 11443 |