Crastin? LW9330 NC010

Manufacturer: Celanese
Produced At: Import/ China
Product Category: PBT
Product No: Crastin? LW9330 NC010
Product Quantity: 25KG / BAG
Product Features: Low Warpage

Product information

Crastin? LW9330 NC010

THERMOPLASTIC POLYESTER RESIN

Product Description:

30% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics

Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Additive	Mold Release
Features	Low Warpage
RoHS Compliance	Contact Manufacturer
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Tensile Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	PBT+SAN-GF30
Resin ID (ISO 1043)	PBT+SAN-GF30

Physical	Nominal Value	Unit	Test Method
Density	1.42	g/cm3	ISO 1183
Melt Mass-Flow Rate (MFR)	13	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (250°C/5.0 kg)	0.610	in3/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	0.60	%
Flow	0.30	%
Water Absorption			ISO 62
Saturation, 73°F, 0.0787 in	1.0	%
Equilibrium, 73°F, 0.0787 in, 50% RH	0.25	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1.42E+6	psi	ISO 527-2
Tensile Stress (Break)	19600	psi	ISO 527-2
Tensile Strain (Break)	2.3	%	ISO 527-2
Flexural Modulus	1.22E+6	psi	ISO 178
Flexural Stress	29000	psi	ISO 178
Poisson's Ratio	0.34		ISO 527
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-40°F	4.3	ft·lb/in2
-22°F	4.3	ft·lb/in2
73°F	4.3	ft·lb/in2
Charpy Unnotched Impact Strength			ISO 179/1eU
-40°F	24	ft·lb/in2
73°F	26	ft·lb/in2
Notched Izod Impact Strength			ISO 180/1A
-40°F	3.3	ft·lb/in2
73°F	3.3	ft·lb/in2
Unnotched Izod Impact Strength			ISO 180/1U
-40°F	21	ft·lb/in2
73°F	21	ft·lb/in2

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)	365	°F	ISO 75-2/A
Ball Pressure Test (383°F)	Pass		IEC 60695-10-2
Melting Temperature 3	437	°F	ISO 11357-3

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Comparative Tracking Index	550	V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Burning Rate 4 (0.0394 in)	1.1	in/min	ISO 3795
Flame Rating			UL 94, IEC 60695-11-10, -20
0.030 in	HB
0.06 in	HB
FMVSS Flammability	B		FMVSS 302

Fill Analysis	Nominal Value	Unit
Melt Density	1.27	g/cm3
Ejection Temperature	338	°F
Specific Heat Capacity of Melt	0.428	Btu/lb/°F
Thermal Conductivity of Melt	1.9	Btu·in/hr/ft2/°F

Injection	Nominal Value	Unit
Drying Temperature	248	°F
Drying Time - Desiccant Dryer	2.0 to 4.0	hr
Suggested Max Moisture	0.040	%
Processing (Melt) Temp	464 to 500	°F
Melt Temperature, Optimum	482	°F
Mold Temperature	86 to 266	°F
Mold Temperature, Optimum	176	°F
Holding Pressure	8700	psi
Back Pressure	As low as possible
Drying Recommended	yes
Hold Pressure Time	3.00	s/mm