Makroblend? UT235 M
Polycarbonate + PET
(PC+PET)-blend, 15% mineral filled, easy flow, low coefficient of linear thermal expansion, easy release, injection molding. Molded parts from UT235M having exceptional dimensional stability.
Filler / Reinforcement | |
Features | - Good Dimensional Stability，Good Flow，Good Mold Release，Low CLTE
|
RoHS Compliance | |
Processing Method | |
Density (73°F) | 1.34 | g/cm3 | ISO 1183 |
Melt Volume-Flow Rate (MVR) (270°C/5.0 kg) | 2.62 | in3/10min | ISO 1133 |
Molding Shrinkage 2 |
|
| ISO 2577 |
Across Flow : 518°F, 0.118 in | 0.50 to 0.60 | % |
|
Flow : 518°F, 0.118 in | 0.50 to 0.60 | % |
|
Water Absorption |
|
| ISO 62 |
Saturation, 73°F | 0.40 | % |
|
Equilibrium, 73°F, 50% RH | 0.20 | % |
|
Tensile Modulus (73°F) | 653000 | psi | ISO 527-2/1 |
Tensile Stress |
|
| ISO 527-2/5 |
Yield, 73°F | 9860 | psi |
|
Break, 73°F | 9720 | psi |
|
Tensile Strain |
|
| ISO 527-2/5 |
Yield, 73°F | 3.5 | % |
|
Break, 73°F | 4.0 | % |
|
Flexural Modulus 3 (73°F) | 674000 | psi | ISO 178 |
Flexural Stress 3 |
|
| ISO 178 |
3.5% Strain, 73°F | 16000 | psi |
|
73°F | 16700 | psi |
|
Flexural Strain at Flexural Strength 4 (73°F) | 5.0 | % | ISO 178 |
Charpy Unnotched Impact Strength |
|
| ISO 179/1eU |
-22°F | 40 | ft·lb/in2 |
|
73°F | 40 | ft·lb/in2 |
|
Unnotched Izod Impact Strength |
|
| ISO 180 |
-22°F | 40 | ft·lb/in2 |
|
73°F | 40 | ft·lb/in2 |
|
Multi-Axial Instrumented Impact Energy (73°F) | 26.6 | ft·lb | ISO 6603-2 |
Multi-Axial Instrumented Impact Peak Force (73°F) | 1010 | lbf | ISO 6603-2 |
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 262 | °F | ISO 75-2/B |
264 psi, Unannealed | 237 | °F | ISO 75-2/A |
Vicat Softening Temperature | 282 | °F | ISO 306/B120 |
CLTE |
|
| ISO 11359-2 |
Flow : 73 to 131°F | 2.5E-5 | in/in/°F |
|
Flow : 73 to 185°F | 2.5E-5 | in/in/°F |
|
Transverse : 73 to 131°F | 2.5E-5 | in/in/°F |
|
Transverse : 73 to 185°F | 2.7E-5 | in/in/°F |
|