Ultramid? A3X2G10

Manufacturer: BASF
Produced At: Europe / China
Product Category: Polyamide 66 Copolymer
Product No: Ultramid A3X2G10
Product Quantity: 25KG / BAG
Product Features: Flame Retardant、Good Electrical Properties、High Stiffness、High Strength、Oil Resistant

Product information

Ultramid? A3X2G10

Polyamide 66

BASF Corporation

Product Description:

A glass fibre reinforced injection moulding grade with improved flame retardance. Flame retardant based on red phosphorus; giving outstanding electrical properties and very high stiffness and strength.

Filler / Reinforcement	Glass Fiber, 50% Filler by Weight
Additive	Flame Retardant
Features	Flame Retardant、Good Electrical Properties、High Stiffness、High Strength、Oil Resistant
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.60	--	g/cm3	ISO 1183
Apparent (Bulk) Density	0.70	--	g/cm3
Melt Volume-Flow Rate (MVR)(275°C/5.0 kg)	1.53	--	in3/10min	ISO 1133
Water Absorption				ISO 62
Saturation, 73°F	3.7 to 4.3	--	%
Equilibrium, 73°F, 50% RH	0.70 to 1.1	--	%
Viscosity Number (96% H2SO4 (Sulphuric Acid))	140	--	cm3/g	ISO 307
Mold Shrinkage - constrained 3	0.40	--	%

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	2.32E+6	1.74E+6	psi	ISO 527-2
Tensile Stress (Break)	26100	18900	psi	ISO 527-2
Tensile Strain (Break)	2.0	3.0	%	ISO 527-2
Tensile Creep Modulus 4 (1000 hr)	--	783000	psi	ISO 899-1
Flexural Modulus	1.89E+6	--	psi	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-22°F	5.2	--	ft·lb/in2
73°F	6.2	7.6	ft·lb/in2
Charpy Unnotched Impact Strength				ISO 179/1eU
-22°F	24	--	ft·lb/in2
73°F	26	26	ft·lb/in2
Notched Izod Impact Strength(73°F)	6.7	9.5	ft·lb/in2	ISO 180/A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed	482	--	°F	ISO 75-2/B
264 psi, Unannealed	482	--	°F	ISO 75-2/A
Melting Temperature	500	--	°F	ISO 11357-3
CLTE				ISO 11359-2
Flow : 73 to 176°F	8.3E-6 to 1.1E-5	--	in/in/°F
Transverse : 73 to 176°F	2.2E-5 to 2.8E-5	--	in/in/°F
Specific Heat	0.311	--	Btu/lb/°F
Thermal Conductivity	2.4	--	Btu·in/hr/ft2/°F	DIN 52612
Maximum Service Temperature - short cycle operation	428	--	°F
Temperature Index - at 50% loss of tensile strength				IEC 60216
-- 5	293	--	°F
-- 6	257	--	°F

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	--	1.0E+10	ohms	IEC 60093
Volume Resistivity	1.0E+15	1.0E+12	ohms·cm	IEC 60093
Electric Strength 7	840	760	V/mil	IEC 60243-1
Relative Permittivity (1 MHz)	3.60	5.00		IEC 60250
Dissipation Factor (1 MHz)	0.020	--		IEC 60250
Comparative Tracking Index (Solution A)	600	--	V	IEC 60112
Flammability	Dry	Conditioned	Unit	Test Method
Glow Wire Flammability Index (0.04 in)	1760	--	°F	IEC 60695-2-12
Oxygen Index	27	--	%	ISO 4589-2
Smoke Density	180	--		ISO 5659-2
Smoke Toxicity - CIT NLP acc. to CEN/TS 45545-2	0.360	--		NF X70-100

Additional Information	Dry	Conditioned
Polymer Abbreviation	PA66-GF50 FR	--

Injection	Dry	Unit
Drying Temperature	176 to 212	°F
Drying Time	4.0	hr
Suggested Max Moisture	0.15	%
Hopper Temperature	176	°F
Rear Temperature	563	°F
Middle Temperature	563	°F
Front Temperature	563	°F
Nozzle Temperature	563	°F
Processing (Melt) Temp	554 to 572	°F
Mold Temperature	176 to 194	°F
Residence Time	< 10.0	min
Screw Speed	< 709	in/min