Amodel? AT-1116 HS

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: Amodel PPA
Product No: Amodel AT-1116 HS
Product Quantity: 25KG / BAG
Product Features: Chemical Resistant，Good Dimensional Stability，Heat Stabilized，High Heat Resistance，Impact Modified

Product information

Amodel? AT-1116 HS

Polyphthalamide

Solvay Specialty Polymers

Product Description:

Amodel? AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass reinforced PPA.

Typical applications include bearings, bearing retainers/cages, housings, chemical processing equipment components, motor frames, sporting equipment, lawn and garden equipment and components that require press-fit or snap-fit assembly.

Black: AT-1116 HS BK 324

Natural: AT-1116 HS NT

Filler / Reinforcement	Glass Fiber, 16% Filler by Weight
Additive	Heat Stabilizer,Impact Modifier
Features	Chemical Resistant,Good Dimensional Stability,Heat Stabilized,High Heat Resistance,Impact Modified
Uses	Automotive Applications,Automotive Electronics,Automotive Under the HoodBearings,Bobbins,Connectors,General Purpose, Industrial Applications,Industrial Parts, Machine/Mechanical Parts,Metal Replacement
RoHS Compliance	RoHS Compliant
Appearance	Black,Natural Color
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.28	--	g/cm3	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	6.0E-3	--	in/in
Across Flow	6.0E-3	--	in/in
Water Absorption (24 hr)	0.20	--	%	ASTM D570

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	940000	1.03E+6	psi	ASTM D638
73°F	1.00E+6	--	psi	ISO 527-2
212°F	970000	--	psi	ISO 527-2
Tensile Stress
Break, 73°F	23200	--	psi	ISO 527-2
Break, 212°F	9500	--	psi	ISO 527-2
--	23300	19000	psi	ASTM D638
Tensile Elongation
Break	3.8	2.8	%	ASTM D638
Break, 73°F	3.7	--	%	ISO 527-2
Break, 212°F	4.2	--	%	ISO 527-2
Flexural Modulus
--	870000	900000	psi	ASTM D790
73°F	970000	--	psi	ISO 178
212°F	720000	--	psi	ISO 178
Flexural Strength
--	32800	29100	psi	ASTM D790
73°F	28600	--	psi	ISO 178
212°F	20500	--	psi	ISO 178
Compressive Strength	18000	--	psi	ASTM D695
Shear Strength	10100	9500	psi	ASTM D732
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength(73°F)	4.3	--	ft·lb/in2	ISO 179/1eA
Charpy Unnotched Impact Strength(73°F)	41	--	ft·lb/in2	ISO 179/1eU
Notched Izod Impact
--	1.8	0.90	ft·lb/in	ASTM D256
73°F	3.8	--	ft·lb/in2	ISO 180/1A
Unnotched Izod Impact
--	18	15	ft·lb/in	ASTM D256
73°F	25	--	ft·lb/in2	ISO 180/1U
Instrumented Dart Impact				ASTM D3763
Energy at Maxumum Load 3	--	12.0	in·lb
Energy at Maxumum Load 4	15.6	--	in·lb
Total Energy	88.8	67.2	in·lb

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
66 psi, Annealed	515	--	°F	ASTM D648
264 psi, Unannealed	497	--	°F	ISO 75-2/A
264 psi, Annealed	489	--	°F	ASTM D648
Peak Melting Temperature	590	--	°F	ASTM D3418
CLTE				ASTM E831
Flow : 32 to 212°F	1.2E-5	--	in/in/°F
Flow : 212 to 392°F	8.9E-6	--	in/in/°F
Transverse : 32 to 212°F	4.2E-5	--	in/in/°F
Transverse : 212 to 392°F	6.7E-5	--	in/in/°F

Injection	Dry	Unit
Drying Temperature	230	°F
Drying Time	4.0	hr
Suggested Max Moisture	0.030 to 0.060	%
Rear Temperature	580 to 605	°F
Front Temperature	600 to 625	°F
Processing (Melt) Temp	610 to 650	°F
Mold Temperature	275	°F
Injection Notes
Storage: Amodel? compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel? resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel? processing guide.