Amodel? AT-6130 HS

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: Amodel PPA
Product No: Amodel AT-6130 HS
Product Quantity: 25KG / BAG
Product Features: Chemical Resistant,Good Flow,Heat Stabilized,High Heat Resistance,High Strength,Hot Water Moldability,Impact Modified,Low Friction,Lubricated,Wear Resistant

Product information

Amodel? AT-6130 HS

Polyphthalamide

Solvay Specialty Polymers

Product Description:

Amodel? AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of Amodel? resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles. The processing window is relatively broad and mold temperatures as low as 150°F (65°C) can be used.

Black: AT-6130 HS BK 324

Natural: AT-6130 HS NT

Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Additive	Heat Stabilizer,Impact Modifier,Lubricant,Mold Release
Features	Chemical Resistant,Good Flow,Heat Stabilized,High Heat Resistance,High Strength,Hot Water Moldability,Impact Modified,Low Friction,Lubricated,Wear Resistant
Uses	Automotive Applications,Automotive Electronics,Automotive Under the Hood,Bearings,Connectors,Fuel Lines,General Purpose,Housings,Industrial Applications,Industrial Parts,Lawn and Garden Equipment,Machine/Mechanical Parts,Metal Replacement,Valves/Valve Parts
RoHS Compliance	RoHS Compliant
Appearance	Black,Natural Color
Forms	Pellets
Processing Method	Water-Heated Mold Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.34	--	g/cm3	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	5.0E-3	--	in/in
Across Flow	8.0E-3	--	in/in
Water Absorption (24 hr)	0.15	--	%	ASTM D570

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	1.35E+6	--	psi	ISO 527-2
Tensile Strength
Break	24200	--	psi	ASTM D638
Break	24600	--	psi	ISO 527-2
Tensile Elongation
Break	3.2	--	%	ASTM D638
Break	3.3	--	%	ISO 527-2
Flexural Modulus
--	1.14E+6	--	psi	ASTM D790
--	1.10E+6	--	psi	ISO 178
Flexural Stress
--	32600	--	psi	ISO 178
Yield	34200	--	psi	ASTM D790
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength	6.0	--	ft·lb/in2	ISO 179/1eA
Notched Izod Impact	2.5	--	ft·lb/in	ASTM D256
Unnotched Izod Impact	26	--	ft·lb/in	ASTM D256

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed	568	--	°F	ISO 75-2/B
264 psi, Unannealed	529	--	°F	ISO 75-2/A
Melting Temperature
--	590	--	°F	ISO 11357-3
--	583	--	°F	ASTM D3418

Injection	Dry	Unit
Drying Temperature	250	°F
Drying Time	4.0	hr
Suggested Max Moisture	0.030 to 0.060	%
Rear Temperature	600 to 615	°F
Front Temperature	620 to 630	°F
Processing (Melt) Temp	610 to 635	°F
Mold Temperature	150 to 200	°F
Injection Rate	Fast
Injection Notes
Injection pressure between 2-4 in/sec (5-10 cm/sec). Adjust the holding pressure to one-half the injection pressure. Storage: Amodel? compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel? resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel? processing guide.