LEXAN? Copolymer 923X
聚碳酸酯
產品說明:
LEXAN923x is a UV stabilized high flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN 923x resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications.
添加劑 | |
特性 | Chlorine Free,沖擊改性,可加工性，良好,快的成型周期,流動性高,無溴,延展性,阻燃性
|
用途 | |
外觀 | |
加工方法 | |
Also Available In | |
密度 / 比重 | 1.19 |
| ASTM D792 |
熔流率（熔體流動速率） (300°C/1.2 kg) | 16 | g/10 min | ASTM D1238 |
收縮率 - 流動 (0.126 in) | 4.0E-3 到 8.0E-3 | in/in | 內部方法 |
拉伸模量 3 | 305000 | psi | ASTM D638 |
抗張強度 4 |
|
| ASTM D638 |
屈服 | 8410 | psi |
|
斷裂 | 8700 | psi |
|
伸長率 4 |
|
| ASTM D638 |
屈服 | 6.0 | % |
|
斷裂 | 110 | % |
|
彎曲模量 5 (1.97 in 跨距) | 348000 | psi | ASTM D790 |
彎曲強度 5 (屈服, 1.97 in 跨距) | 13100 | psi | ASTM D790 |
懸壁梁缺口沖擊強度 |
|
| ASTM D256 |
-22°F | 12 | ft·lb/in |
|
73°F | 15 | ft·lb/in |
|
裝有測量儀表的落鏢沖擊 (73°F, Total Energy) | 575 | in·lb | ASTM D3763 |
載荷下熱變形溫度 (264 psi, 未退火, 0.126 in) | 253 | °F | ASTM D648 |
維卡軟化溫度 | 284 | °F | ASTM D1525 6 |
線形熱膨脹系數 |
|
| ASTM E831 |
流動 : -40 到 104°F | 3.4E-5 | in/in/°F |
|
橫向 : -40 到 104°F | 3.4E-5 | in/in/°F |
|
RTI Elec | 257 | °F | UL 746 |
RTI Imp | 239 | °F | UL 746 |
RTI | 248 | °F | UL 746 |
UL 阻燃等級 |
|
| UL 94 |
0.06 in | V-0 |
|
|
0.12 in | 5VA |
|
|
灼熱絲易燃指數 (0.06 in) | 1760 | °F | IEC 60695-2-12 |
熱燈絲點火溫度 |
|
| IEC 60695-2-13 |
0.06 in | 1520 | °F |
|
0.12 in | 1520 | °F |
|
干燥溫度 | 248 | °F |
|
干燥時間 | 3.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
建議注射量 | 40 到 60 | % |
|
料筒后部溫度 | 518 到 563 | °F |
|
料筒中部溫度 | 536 到 581 | °F |
|
料筒前部溫度 | 563 到 599 | °F |
|
射嘴溫度 | 554 到 590 | °F |
|
加工（熔體）溫度 | 563 到 599 | °F |
|
模具溫度 | 158 到 203 | °F |
|
背壓 | 43.5 到 102 | psi |
|
螺桿轉速 | 40 到 70 | rpm |
|
排氣孔深度 | 9.8E-4 到 3.0E-3 | in |
|
如需沙伯基礎（SABIC）原廠物性表及相關文件，請聯系我們工作人員，謝謝！