Plexiglas? Resist AG 100
聚甲基丙烯酸甲酯-丙烯酸
PLEXIGLAS? Resist AG 100 is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).
Properties
PLEXIGLAS? molding compounds have the following typical properties:
PLEXIGLAS? Resist AG 100 is characterized by the following additional properties:
添加劑 | |
特性 | |
用途 | |
外觀 | - Transparent Green、Transparent Grey、清晰/透明
|
形式 | |
加工方法 | |
密度 | 1.16 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） |
|
| ISO 1133 |
230°C/3.8 kg | 0.0671 | in3/10min |
|
260°C/3.8 kg | 0.470 | in3/10min |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 1.5 | % |
|
平衡, 73°F, 50% RH | 0.50 | % |
|
拉伸模量 | 319000 | psi | ISO 527-2/1 |
拉伸應力 (屈服) | 7980 | psi | ISO 527-2/50 |
拉伸應變 (屈服) | 5.0 | % | ISO 527-2/50 |
標稱拉伸斷裂應變 | 45 | % | ISO 527-2 |
簡支梁無缺口沖擊強度 (73°F) | 57 | ft·lb/in2 | ISO 179/1eU |
熱變形溫度 |
|
|
|
66 psi, 未退火 | 221 | °F | ISO 75-2/B |
264 psi, 未退火 | 212 | °F | ISO 75-2/A |
玻璃轉化溫度 | 234 | °F | ISO 11357-2 |
維卡軟化溫度 | 221 | °F | ISO 306/B50 |
線形熱膨脹系數(shù) - 流動 (32 到 122°F) | 6.1E-5 | in/in/°F | ISO 11359-2 |
UL 阻燃等級 (0.06 in) | HB |
| IEC 707 |
折射率 | 1.490 |
| ISO 489 |
透射率 2 | 91.0 | % | ISO 13468-2 |
霧度 | 0.70 | % | ASTM D1003 |
干燥溫度 | 158 到 176 | °F |
|
干燥時間 | 3.0 到 4.0 | hr |
|
加工（熔體）溫度 | 455 到 518 | °F |
|
模具溫度 | 140 到 176 | °F |
|
干燥溫度 | 158 到 176 | °F |
|
干燥時間 | 3.0 到 4.0 | hr |
|
熔體溫度 | 455 到 518 | °F |
|
口模溫度 | 464 | °F |
|
如需德固賽原廠物性表及相關文件，請聯(lián)系我們工作人員，謝謝！