Stanyl? TS300
聚酰胺 46
產(chǎn)品說明:
Special Features:
Stanyl? is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
| 密度 | 1.18 | -- | g/cm3 | ISO 1183 |
| 收縮率 |
|
|
| ISO 294-4 |
| 橫向流量 | 2.0 | -- | % |
|
| 流量 | 2.0 | -- | % |
|
| 吸水率 |
|
|
| ISO 62 |
| 飽和, 73°F | 14 | -- | % |
|
| 平衡, 73°F, 50% RH | 3.7 | -- | % |
|
| 粘數(shù) | 185 | -- | cm3/g | ISO 307 |
| 拉伸模量 |
|
|
| ISO 527-2 |
| -- | 479000 | 145000 | psi |
|
| 248°F | 116000 | -- | psi |
|
| 320°F | 94300 | -- | psi |
|
| 356°F | 87000 | -- | psi |
|
| 392°F | 72500 | -- | psi |
|
| 拉伸應(yīng)力 |
|
|
| ISO 527-2 |
| 屈服 | 14500 | 7980 | psi |
|
| 屈服, 248°F | 7250 | -- | psi |
|
| 屈服, 320°F | 5800 | -- | psi |
|
| 屈服, 356°F | 5080 | -- | psi |
|
| 屈服, 392°F | 4350 | -- | psi |
|
| 拉伸應(yīng)變 (屈服) | 10 | 20 | % | ISO 527-2 |
| 標(biāo)稱拉伸斷裂應(yīng)變 |
|
|
| ISO 527-2 |
| -- | 40 | > 50 | % |
|
| 356°F | > 50 | -- | % |
|
| 392°F | > 50 | -- | % |
|
| 彎曲模量 |
|
|
| ISO 178 |
| -- | 435000 | 131000 | psi |
|
| 248°F | 116000 | -- | psi |
|
| 320°F | 87000 | -- | psi |
|
| 簡支梁缺口沖擊強度 |
|
|
| ISO 179/1eA |
| -22°F | 1.9 | 1.9 | ft·lb/in2 |
|
| 73°F | 4.8 | 17 | ft·lb/in2 |
|
| 簡支梁無缺口沖擊強度 |
|
|
| ISO 179/1eU |
| -22°F | 無斷裂 | 無斷裂 |
|
|
| 73°F | 無斷裂 | 無斷裂 |
|
|
| 懸壁梁缺口沖擊強度 |
|
|
| ISO 180/1A |
| -40°F | 1.9 | 1.9 | ft·lb/in2 |
|
| 73°F | 4.8 | 17 | ft·lb/in2 |
|
| 熱變形溫度 |
|
|
|
|
| 66 psi, 未退火 | 536 | -- | °F | ISO 75-2/B |
| 264 psi, 未退火 | 374 | -- | °F | ISO 75-2/A |
| 玻璃轉(zhuǎn)化溫度 2 | 167 | -- | °F | ISO 11357-2 |
| 維卡軟化溫度 | 554 | -- | °F | ISO 306/B50 |
| 熔融溫度 2 | 563 | -- | °F | ISO 11357-3 |
| 線形熱膨脹系數(shù) |
|
|
| ISO 11359-2 |
| 流動 | 4.7E-5 | -- | in/in/°F |
|
| 橫向 | 6.1E-5 | -- | in/in/°F |
|
| 干燥溫度 | 176 | °F |
| 干燥時間 | 4.0 到 8.0 | hr |
| 料筒后部溫度 | 536 到 608 | °F |
| 料筒中部溫度 | 572 到 608 | °F |
| 料筒前部溫度 | 572 到 608 | °F |
| 射嘴溫度 | 572 到 608 | °F |
| 加工（熔體）溫度 | 590 到 608 | °F |
| 模具溫度 | 176 到 248 | °F |
| 注射速度 | 中等偏快 |
|
| 背壓 | 290 到 1450 | psi |
| 螺桿壓縮比 | 2.5:1.0 |
|
如需恩驊力（Envalior）原廠物性表及相關(guān)文件，請聯(lián)系我司工作人員，謝謝！