Texin? RxT65D
熱塑性聚氨酯彈性體（聚醚）
Texin RxT65D resin is an aromatic polyether-based thermoplastic polyurethane. It can be processed by injection molding, extrusion or blow molding.
特性 | |
用途 | - 薄膜、墊圈、管件、連接器、密封件、型材、醫療/護理用品
|
機構評級 | |
加工方法 | |
密度 / 比重 |
|
|
|
-- | 1.17 |
| ASTM D792 |
-- | 1.17 | g/cm3 | ISO 1183 |
熔流率（熔體流動速率） (220°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
收縮率 |
|
|
|
流動 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
橫向流動 : 0.100 in | 8.0E-3 | in/in | ASTM D955 |
橫向流量 : 0.100 in | 0.80 | % | ISO 2577 |
流量 : 0.100 in | 0.80 | % | ISO 2577 |
肖氏硬度 (邵氏 D) | 65 |
| ASTM D2240, ISO 868 |
彎曲模量 (73°F) | 61000 | psi | ASTM D790, ISO 178 |
泰伯耐磨性 |
|
|
|
1000 Cycles, 1000 g, H-18 轉輪 | 75.0 | mg | ASTM D1044 |
1000 Cycles, 1000 g, H-18 轉輪 | 75.0 | mg | ISO 4649 |
拉伸應力 |
|
| ASTM D412, ISO 37 |
100%應變 | 3600 | psi |
|
300%應變 | 6110 | psi |
|
抗張強度 (屈服) | 7500 | psi | ASTM D412, ISO 37 |
伸長率 (斷裂) | 370 | % | ASTM D412, ISO 37 |
撕裂強度 |
|
|
|
-- 2 | 1200 | lbf/in | ASTM D624 |
-- | 1200 | lbf/in | ISO 34-1 |
壓縮永久變形 3 |
|
| ASTM D395B, ISO 815 |
73°F, 22 hr | 20 | % |
|
158°F, 22 hr | 35 | % |
|
維卡軟化溫度 | 280 | °F | ISO 306/50, ASTM D1525 4 |
黃度指數 |
|
|
|
-- | < 10 | YI | ASTM E313 |
-- | < 10 | YI | DIN 6167 |
干燥溫度 - 熱風干燥機 | 199 到 219 | °F |
|
干燥時間 - 熱風干燥機 | 2.0 | hr |
|
建議的最大水分含量 | < 0.030 | % |
|
料筒后部溫度 | 390 到 410 | °F |
|
料筒中部溫度 | 396 到 415 | °F |
|
料筒前部溫度 | 396 到 415 | °F |
|
射嘴溫度 | 399 到 421 | °F |
|
加工（熔體）溫度 | 399 到 421 | °F |
|
模具溫度 | 61 到 100 | °F |
|
注塑壓力 | 6000 到 15000 | psi |
|
注射速度 | 中等 |
|
|
背壓 | < 800 | psi |
|
螺桿轉速 | 40 到 80 | rpm |
|
墊層 | < 0.125 | in |
|
Hold Pressure: 60 to 80% of Injection Pressure |
干燥溫度 | 199 到 219 | °F |
|
干燥時間 | 2.0 | hr |
|
料筒1區溫度 | 370 到 390 | °F |
|
料筒2區溫度 | 390 到 410 | °F |
|
料筒3區溫度 | 390 到 410 | °F |
|
熔體溫度 | 399 到 421 | °F |
|
口模溫度 | 390 到 421 | °F |
|
如需科思創原廠物性表及相關文件，請聯系我們工作人員，謝謝！