ForTii? LDS81
Polyamide 4T
產品說明:
35% Glass Reinforced, Laser Direct Structuring (LDS)
Special Features:
Used In:
ForTii? is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii? in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €" and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.
填料/增強材料 | |
添加劑 | |
用途 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.57 | -- | g/cm3 | ISO 1183 |
吸水率 (平衡, 73°F, 50% RH) | 1.7 | -- | % | ISO 62 |
拉伸模量 | 1.81E+6 | 1.81E+6 | psi | ISO 527-2 |
拉伸應力 (斷裂) | 18900 | 18900 | psi | ISO 527-2 |
拉伸應變 (斷裂) | 1.2 | 1.2 | % | ISO 527-2 |
彎曲模量 | 1.74E+6 | -- | psi | ISO 178 |
彎曲應力 | 31900 | -- | psi | ISO 178 |
簡支梁缺口沖擊強度 (73°F) | 1.9 | 1.9 | ft·lb/in2 | ISO 179/1eA |
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 599 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 572 | -- | °F | ISO 75-2/A |
玻璃轉化溫度 2 | 257 | -- | °F | ISO 11357-2 |
熔融溫度 2 | 617 | -- | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
|
| ASTM D696 |
流動 | 1.4E-5 | -- | in/in/°F |
|
橫向 | 2.5E-5 | -- | in/in/°F |
|
體積電阻率 | > 1.0E+15 | > 1.0E+15 | ohms·cm | IEC 60093 |
介電強度 | 660 | 660 | V/mil | IEC 60243-1 |
相對電容率 (1.00 GHz) | 4.00 | -- |
| IEC 60250 |
可燃性等級 (0.03 in) | HB | -- |
| IEC 60695-11-10, -20 |
干燥溫度 | 212 | °F |
|
干燥時間 | 2.0 | hr |
|
料筒后部溫度 | 608 到 626 | °F |
|
料筒中部溫度 | 617 到 635 | °F |
|
料筒前部溫度 | 626 到 635 | °F |
|
射嘴溫度 | 626 到 635 | °F |
|
加工（熔體）溫度 | 626 到 644 | °F |
|
模具溫度 | 212 到 302 | °F |
|
注射速度 | 中等偏快 |
|
|
背壓 | 72.5 到 435 | psi |
|
螺桿壓縮比 | 2.5:1.0 |
|
|