Ultrason? S 2010
聚砜
產品說明:
Ultrason S 2010 is an unreinforced, medium viscosity standard injection molding PSU grade. It flows readily and offers outstanding heat resistance and dimensional stability. Typical applications include automotive applications such as fuse encapsulation, connectors, heating system and headlight components and household applications requiring high heat resistance.
特性 | |
用途 | |
機構評級 | |
RoHS 合規性 | |
形式 | |
加工方法 | |
多點數據 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 | 1.23 | g/cm3 | ISO 1183 |
溶化體積流率（MVR） (360°C/10.0 kg) | 5.49 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.72 | % |
|
流量 | 0.68 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.80 | % |
|
平衡, 73°F, 50% RH | 0.30 | % |
|
球壓硬度 | 19600 | psi | ISO 2039-1 |
拉伸模量 (73°F) | 370000 | psi | ISO 527-2 |
拉伸應力 (屈服, 73°F) | 10900 | psi | ISO 527-2 |
拉伸應變 (屈服, 73°F) | 6.0 | % | ISO 527-2 |
簡支梁缺口沖擊強度 |
|
| ISO 179 |
-22°F | 2.9 | ft·lb/in2 |
|
73°F | 2.6 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
| ISO 179 |
-22°F | 無斷裂 |
|
|
73°F | 無斷裂 |
|
|
懸壁梁缺口沖擊強度 |
|
| ISO 180 |
-22°F | 2.9 | ft·lb/in2 |
|
73°F | 2.6 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 349 | °F | ISO 75-2/A |
線形熱膨脹系數 - 流動 | 2.9E-5 | in/in/°F |
|
RTI Elec |
|
| UL 746 |
0.06 in | 311 | °F |
|
0.13 in | 311 | °F |
|
RTI Imp |
|
| UL 746 |
0.06 in | 266 | °F |
|
0.13 in | 266 | °F |
|
RTI |
|
| UL 746 |
0.06 in | 311 | °F |
|
0.13 in | 311 | °F |
|
表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
介電強度 | 1000 | V/mil | IEC 60243-1 |
介電常數 |
|
| IEC 60250 |
100 Hz | 3.10 |
|
|
1 MHz | 3.10 |
|
|
耗散因數 |
|
| IEC 60250 |
100 Hz | 8.0E-4 |
|
|
1 MHz | 6.4E-3 |
|
|
漏電起痕指數 | 125 | V | IEC 60112 |
UL 阻燃等級 |
|
| UL 94 |
0.06 in | HB |
|
|
0.13 in | V-2 |
|
|
干燥溫度 | 266 到 302 | °F |
|
干燥時間 | 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
加工（熔體）溫度 | 644 到 734 | °F |
|
模具溫度 | 284 到 356 | °F |
|
注塑壓力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|