Ultraform? W 2320 003
聚甲醛（POM）共聚物
產品說明:
Very free-flowing, rapidly solidifying grade for use where processing is extremely difficult but mechanical properties are lower.
特性 | |
機構評級 | |
RoHS 合規性 | |
形式 | |
加工方法 | |
多點數據 | Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Heat vs. Temperature (ISO 11403-2) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2) |
樹脂ID (ISO 1043) | |
密度 | 1.40 | g/cm3 | ISO 1183 |
溶化體積流率（MVR） (190°C/2.16 kg) | 1.53 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 2.1 | % |
|
流量 | 2.0 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.80 | % |
|
平衡, 73°F, 50% RH | 0.20 | % |
|
球壓硬度 (H 358/30) | 21000 | psi | ISO 2039-1 |
拉伸模量 | 406000 | psi | ISO 527-2 |
拉伸應力 (屈服) | 9430 | psi | ISO 527-2/50 |
拉伸應變 (屈服) | 7.5 | % | ISO 527-2/50 |
標稱拉伸斷裂應變 | 24 | % | ISO 527-2/50 |
拉伸蠕變模量 3 (1000 hr) | 196000 | psi | ISO 899-1 |
簡支梁缺口沖擊強度 |
|
| ISO 179/1eA |
-22°F | 1.9 | ft·lb/in2 |
|
73°F | 2.4 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
| ISO 179/1eU |
-22°F | 71 | ft·lb/in2 |
|
73°F | 71 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 212 | °F | ISO 75-2/A |
熔融溫度 | 333 | °F | ISO 11357-3 |
線形熱膨脹系數 - 流動 (73 到 131°F) | 6.1E-5 | in/in/°F | ISO 11359-2 |
最高使用溫度 - short cycle operation | 212 | °F |
|
表面電阻率 | 1.0E+13 | ohms | IEC 60093 |
體積電阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
相對電容率 (1 MHz) | 3.80 |
| IEC 60250 |
耗散因數 (1 MHz) | 5.0E-3 |
| IEC 60250 |
漏電起痕指數 (解決方案 A) | 600 | V | IEC 60112 |
可燃性等級 (0.06 in) | HB |
| IEC 60695-11-10, -20 |
ISO Type | POM-K, M-GNR, 05-002 |
| ISO 9988-1 |
干燥溫度 | 212 | °F |
|
干燥時間 | 3.0 | hr |
|
建議的最大水分含量 | 0.20 | % |
|
料斗溫度 | 392 | °F |
|
料筒后部溫度 | 392 | °F |
|
料筒中部溫度 | 392 | °F |
|
料筒前部溫度 | 392 | °F |
|
射嘴溫度 | 392 | °F |
|
加工（熔體）溫度 | 374 到 446 | °F |
|
模具溫度 | 140 到 248 | °F |
|
Residence Time | < 10.0 | min |
|
Screw Speed | < 709 | in/min |
|
如需巴斯夫原廠物性表及相關文件，請聯系我們工作人員，謝謝！