Ixef? DW-1022

產品產商：索爾維（SOLVAY）
產品產地：進口/中國
產品類別：IXEF PARA
產品型號：Ixef DW-1022
產品規格：25KG/包
產品特性：超強剛性，尺寸穩定性良好，出色的外觀，低吸濕性，高強度，好的消毒性，良好的抗蠕變性，流動性高，耐化學性良好，通用

產品信息

Ixef? DW-1022

聚丙烯酰胺

Solvay Specialty Polymers

產品說明:

Ixef? DW-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.

Ixef? DW-1022 is approved for use in potable water in France, Germany, the United States and the United Kingdom.

Black: DW-1022 BK 000

Black: DW-1022 BK 001

Natural: DW-1022 NT 000

填料/增強材料	玻璃纖維增強材料, 50% 填料按重量
特性	超強剛性,尺寸穩定性良好，出色的外觀，低吸濕性，高強度，好的消毒性，良好的抗蠕變性，流動性高，耐化學性良好，通用
用途	電器用具，高光應用，醫療器材，飲用水應用
機構評級	ACS 未評級DVGW W270FDA 21 CFR 176.170，表 2，狀態 CFDA 21 CFR 176.170，表2，狀態 BFDA 21 CFR 176.170，表2，狀態DFDA 21 CFR 176.170，表2，狀態GFDA 21 CFR 176.170，表2，狀態FFDA 21 CFR 176.170，表2，狀態HKTW 未評級 3NSF 51 4NSF 61 5WRAS 未評級 at 85°C歐洲 No 10/2011
RoHS 合規性	RoHS 合規
外觀	黑色，自然色
形式	粒子
加工方法	注射成型

物理性能	干燥	調節后的	單位制	測試方法
密度	1.64	--	g/cm3	ISO 1183
收縮率	0.10 到 0.30	--	%	ISO 294-4
吸水率 (73°F, 24 hr)	0.16	--	%	ISO 62

機械性能	干燥	調節后的	單位制	測試方法
拉伸模量	2.83E+6	2.83E+6	psi	ISO 527-2
拉伸應力 (斷裂)	40600	37700	psi	ISO 527-2
拉伸應變 (斷裂)	1.9	2.2	%	ISO 527-2
彎曲模量	2.68E+6	--	psi	ISO 178
彎曲應力	55100	--	psi	ISO 178
沖擊性能	干燥	調節后的	單位制	測試方法
懸壁梁缺口沖擊強度	2.1	--	ft·lb/in	ASTM D256
無缺口懸臂梁沖擊	16	--	ft·lb/in	ASTM D256

熱性能	干燥	調節后的	單位制	測試方法
熱變形溫度 (264 psi, 未退火)	446	--	°F	ISO 75-2/A
線形熱膨脹系數 - 流動	8.3E-6	--	in/in/°F	ISO 11359-2

補充信息	干燥	調節后的
吸水性 - Equil, 65% RH	--

注射	干燥	單位制
干燥溫度	248	°F
干燥時間	0.50 到 1.5	hr
料筒后部溫度	482 到 500	°F
料筒前部溫度	500 到 554	°F
射嘴溫度	500 到 554	°F
加工（熔體）溫度	536	°F
模具溫度	248 到 284	°F
注射速度	快速
注射說明
Hot runners: 250°C to 260°C (482°C to 500°F) Storage Ixef? compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef? resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef? processing guide. Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding Ixef? DW-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).